301 Stainless Steel Strips Cold Rolled Stainless Steel Strip Price
301 Stainless Steel Strip Features:
The 301 stainless steel belt is a kind of metastable austenitic stainless steel with complete austenitic structure under the condition of sufficient solution. In stainless steel, 301 is the most easily cold deformation strengthening steel grade, through the cold deformation processing can make the strength of steel, hardness, and retain enough plastic and toughness, together with the steel under the condition of the atmosphere with good rust resistance, but the poor corrosion resistance, reducing medium in acid and alkali salt chemical medium corrosion resistance is poorer, therefore is not recommended for corrosion harsh environment.
The 301 is mainly used in cold working condition for equipment parts that bear high loads and want to reduce the weight of the equipment and do not rust. In addition, this steel is easy to produce work hardening when impacted by external forces and can absorb more impact energy, which will provide a more reliable safety guarantee for equipment and personnel.
The 301 is prone to work hardening during deformation and is used in places requiring higher strength
301 Stainless Steel Strip Chemical Composition (%):
| Element | Minimum percentage | Maximum percentage |
| C | – | 0.15 |
| Si | – | 1.0 |
| Mn | – | 2.0 |
| P | – | 0.045 |
| S | – | 0.03 |
| Cr | 16 | 18 |
| Ni | 6 | 8 |
301 Stainless Steel Strip Mechanical Properties:
| | Metric | Imperial |
| Tensile Strength, Ultimate | 827 MPa | 120 ksi |
| Tensile Strength, Yield | 310 MPa | 45 ksi |
| Elongation at Break (in 2") | 60% | 60% |
| Rockwell Hardness | B86 | B86 |
301 Stainless Steel Strip Applications:
This stainless steel grade demonstrates excellent corrosion resistance, high strength, and good ductility. High hardness combined with high strength achieved through cold working make 301 suitable for structural applications in aircraft and its excellent corrosion resistance meet food service equipment standards.
301 stainless is typically used in aircraft structural components, trailer bodies, trim for architecture and automotive, roof drainage, conveyor belts, train cars, appliances, cooking utensils, and more.
301 Stainless Steel Strip Information:
1-1: What is the difference between 301 and 304 stainless steel grades?
The amount of chromium and nickel in 301 stainless steel is lower than in 304. The reduction of chromium and nickel extends the range of cold work-hardening capability which in turn produces higher tensile strengths.
1-2: How does this grade perform in lower temperature conditions?
301 performs well in lower temperature conditions, especially where tensile strength is considered. For example, in the annealed condition 301 demonstrates an ultimate yield strength of 758 MPa (110 ksi). Once cold worked, that can increase to 1,276 MPa (185 ksi). High strengths achieved through cold work-hardening make this grade suitable for structural applications in colder temperatures.
1-3: What is austenitic steel?
Austenitic stainless steel is a type of stainless steel. The other types of stainless steel are: ferritic, martensitic, duplex, and precipitation hardened. These 5 stainless steel classes are determined by their crystalline structures.